Product Name: JHD 1052505 UV
Description:
J-HD 1052505 UV is an HDPE copolymer manufactured using Spherilene Gas-Phase Technology. It is an injection molding grade suitable for applications that require good physical properties even at low temperatures, like pails, containers, and technical moldings.
Main Applications:
- Containers
Additives:
- JHD-1052505: Thermal Antioxidant (Process Stabilizer), Catalyst Neutralizer (acid scavenger, lubricant)
- JHD-1052505 UV: Thermal Antioxidant (Process Stabilizer), Antiblocking Agent, Catalyst Neutralizer (acid scavenger, lubricant), UV Stabilizer
Material Properties
Resin Properties
| Property | Unit | Typical Value | Test Method |
|---|---|---|---|
| Melt Index (190°C/2.16Kg) | g/10 min | 5 | D1238 |
| Density | g/ml | 0.952 | D1505 |
Thermal Properties
| Property | Unit | Typical Value | Test Method |
|---|---|---|---|
| Vicat Softening Point | °C | 124 | D1525 |
Molded Properties
| Property | Unit | Typical Value | Test Method |
|---|---|---|---|
| Flexural Modulus | MPa | 1200 | D790 |
| Tensile Strength at Yield | MPa | 27 | D638 |
| Tensile Strength at Break | MPa | 13 | D638 |
| H.D.T | °C | 67 | D648 |
| Notched Izod Impact @ 23°C | J/m | 29 | D256/A |
Additional Notes
This data consists of typical values and is not to be considered as product specifications.
Be the first to review “JHD 1052505 UV”
Related products
HDPE
"A107746" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, very good impact strength, and optimum stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A108255" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, is easily processable, has high stiffness, and provides good stress cracking resistance (ESCR) with an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S5020 is a high-density polyethylene with a broad molecular weight distribution, specially developed for small blow-molded bottles. Produced with 1-hexene as a co-monomer, it offers high stiffness, easy flow, very good ESCR, chemical resistance, and sufficient impact strength. HDPE S5020 is recommended for multipurpose blow molding processes and has been manufactured under Basell license.
HDPE
HDPE S5510 is a high-density polyethylene, specially developed for large parts blow molding. Produced with 1-hexene as a co-monomer, it offers high stiffness, good processability, excellent parison melt strength, and good ESCR. HDPE S5510 has been manufactured under Basell license.
HDPE
"A 107750" is a high-density polyethylene with propylene as comonomer. It is a medium molar mass with a narrow molar mass distribution. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
T-HD 104440 EA is a high-density polyethylene copolymer suitable as a base resin for crosslinked polyethylene pipes.
HDPE
"A107260" is a high-density polyethylene with Propylene as comonomer. It is very easy flowing, high density, hardness and stiffness, largely warpage-free, for mass product articles in rapid shot frequency. Stabilization: Ca-Stearate, MgO, Irganox1010, UM V13.
HDPE
"AGC107260" is a high-density polyethylene with Propylene as comonomer. The product has good impact strength, good stress cracking resistance (ESCR), low warping, and good flow ability, as well as high density, hardness, and stiffness. Stabilization: Ca-Stearate, Irganox1010.
Reviews
There are no reviews yet.