“A106255” is a high-density polyethylene with Butene-1 as comonomer. It is a special grade for particularly high requirements like low temperature impact strength and stacking, good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168, HOE Wax PED191.
Applications:
- For large containers, e.g., ring drums with 220 liters capacity.
Properties Table:
| No. | Property | Units | Test Method | Value |
|---|---|---|---|---|
| 1 | MFI (190°C/5Kg) | g/10min | ISO 1133 | ≤ 0.1 |
| 2 | MFI (190°C/21.6Kg) | g/10min | ISO 1133 | 2.2 ± 0.2 |
| 3 | Density | g/cm³ | ISO 1183 | 0.950 ± 0.002 |
| 4 | Notched Impact Strength | mJ/mm² | ISO 179/1eA | ≥ 45 |
| 5 | Swell Ratio | % | Internal Method | 145 ± 20 |
Be the first to review “A106255”
Related products
HDPE
"A105010 T2N" is a natural-colored high-density polyethylene with Butene-1 as comonomer. The product is classified as PE100 and shows good stress crack resistance properties (ESCR) combined with good impact strength. Stabilization: Ca-Stearate, Zn-Stearate, Irganox1010, Irgafos168.
HDPE
T-HD 104440 EA is a high-density polyethylene copolymer suitable as a base resin for crosslinked polyethylene pipes.
HDPE
"AGC107260" is a high-density polyethylene with Propylene as comonomer. The product has good impact strength, good stress cracking resistance (ESCR), low warping, and good flow ability, as well as high density, hardness, and stiffness. Stabilization: Ca-Stearate, Irganox1010.
HDPE
"A109450F" is a high-density polyethylene with Butene-1 as comonomer. It is a high molar mass for blown film with, in comparison to EX4, lower stiffness and increased tenacity. The product has good toughness, low gel level, and good tear strength. Stabilization: Ca-Stearate, Zn-Stearate, Irgafos168.
HDPE
"A 107750" is a high-density polyethylene with propylene as comonomer. It is a medium molar mass with a narrow molar mass distribution. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A104750" is a high-density polyethylene with Butene-1 as comonomer. It has high impact strength and slightly lower stiffness than BL3, with high stress cracking resistance (ESCR) even in contact with surfactants. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S5020 is a high-density polyethylene with a broad molecular weight distribution, specially developed for small blow-molded bottles. Produced with 1-hexene as a co-monomer, it offers high stiffness, easy flow, very good ESCR, chemical resistance, and sufficient impact strength. HDPE S5020 is recommended for multipurpose blow molding processes and has been manufactured under Basell license.
HDPE
HDPE S4265 is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing intermediate bulk containers (IBC) for the packaging of dangerous goods, large blow molding parts, and jerry cans. This grade, produced with a 1-hexene co-monomer, offers very good creep strength, chemical resistance, environmental stress cracking resistance (ESCR), good processability, and stiffness.