Product Name: T-HD 104005 EA
Description: T-HD 104005 EA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use as pipe coating applications. T-HD 104005 EA has the following characteristics:
- Good impact strength and chemical resistance
- High ESCR
Applications:
- Pipe coating applications
Physical and Mechanical Properties:
| Property | Unit | Test Method | Typical Value |
|---|---|---|---|
| MELT FLOW INDEX (2.16KG) | g/10min | ASTM D-1238 | 0.5 |
| DENSITY | gr/cm³ | ASTM D-1505 | 0.940 |
| TENSILE STRESS AT YIELD | MPA | ASTM D-638 | 17 |
| TENSILE STRESS AT BREAK | MPA | ASTM D-638 | 26 |
| ELONGATION AT BREAK | % | ASTM D-638 | 600 |
| O.I.T. | MIN | ASTM D-3895 | 45 |
| HARDNESS | – | ASTM D-2240 | 55 |
| MELTING POINT | °C | ASTM D-1525 | 125 |
| VICAT SOFTENING POINT | °C | ASTM D-1525 | 115 |
All above-mentioned data are typical values and are not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).
Grade Suffix (Additives Indication):
- EA: GENERAL ANTIOXIDANT
Be the first to review “T-HD 104005 EA”
Related products
HDPE
"A107260" is a high-density polyethylene with Propylene as comonomer. It is very easy flowing, high density, hardness and stiffness, largely warpage-free, for mass product articles in rapid shot frequency. Stabilization: Ca-Stearate, MgO, Irganox1010, UM V13.
HDPE
HDPE S5510 is a high-density polyethylene, specially developed for large parts blow molding. Produced with 1-hexene as a co-monomer, it offers high stiffness, good processability, excellent parison melt strength, and good ESCR. HDPE S5510 has been manufactured under Basell license.
HDPE
"A107255" is a high-density polyethylene with Butene-1 as comonomer. It is a high molar mass material with very good impact strength and stiffness, good stress cracking resistance (ESCR), and provides an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168, HOE Wax PED191.
HDPE
HDPE S5110 is a high molecular weight, high-density polyethylene with broad molecular weight distribution and 1-hexene as a co-monomer, specially developed for producing thin films with excellent strength and rigidity. This product is suitable for manufacturing high-strength grocery sacks, shopping bags, and high-quality thin films for uni/multi-wall packaging. Films produced with this grade can be readily treated and printed for high-quality graphics.
HDPE
T-HD 103840 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use in rotational molding applications. T-HD 103840 UA has the following characteristics:
HDPE
"A107250" is a high-density polyethylene with Propylene as comonomer. It is easy flowing, low warpage, less hard and stiff than I1. Stabilization: Ca-Stearate, Irganox1010.
HDPE
"A109455F" is a high-density polyethylene with Butene-1 as comonomer. It is a high molar mass for blown film with very high stiffness and good tenacity. Stabilization: Ca-Stearate, Zn-Stearate, Irgafos168.
HDPE
T-HD 105218 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer.