J-10CRP100 Black
Product data sheet for HDPE made via Hostalen Process.
Characteristic Properties:
- Grade: J-10CRP100 Black (PE100 Black)
- Density: 0.955 – 0.959 g/cm³
- Melt Flow Rate (MFR): 0.20 – 0.24 g/10 min (190°C/5 kg)
Main Applications:
- Top-quality PE100 pressure pipes for gas and water transportation at higher pressures or with thinner walls than PE80
Additives:
- Antioxidant / Process stabilizer
- Lubricant (processing aid) / Acid scavenger
- Carbon Black
Material Properties
| Test/Composition | Typical Value | Unit | ASTM Method |
|---|---|---|---|
| Density | 0.947 | g/cm³ | ISO1183 |
| FRR 21.6/5 | 28 | – | – |
| Hydrostatic Strength (80°C) | 5000 (4.5N/mm²) | h | ISO1167 |
| MFR190°/21.6 | 6.2 | g/10 min | ISO1133 |
| MFR190°/5 | 0.22 | g/10 min | ISO1133 |
| Notched Impact @ 23°C | 24 | mJ/mm² | ISO179/1eA |
Additional Notes:
- Material Properties: These data are typical values and should not be construed as actual product specifications. Users should conduct their own tests to confirm these properties.
- Testing Conditions:
- Test specimens are taken from compression molded sheets at 23°C.
- FRR values are statistical and calculated by dividing MFR values.
- Notch Impact Test specimen from compressed molded sheet at 23°C; the data quoted are average values.
Be the first to review “J-10CRP100 Black”
Related products
HDPE
"A107250" is a high-density polyethylene with Propylene as comonomer. It is easy flowing, low warpage, less hard and stiff than I1. Stabilization: Ca-Stearate, Irganox1010.
HDPE
HDPE1080 is a high molecular weight, high-density polyethylene (HDPE) with high melt viscosity for extrusion. This grade, which is produced by 1-hexene co-monomer, is classified as HDPE1080 and provides excellent stress crack resistance properties (ESCR) combined with very good long-term hydrostatic strength and good processability.
HDPE
"A105010 T2N" is a natural-colored high-density polyethylene with Butene-1 as comonomer. The product is classified as PE100 and shows good stress crack resistance properties (ESCR) combined with good impact strength. Stabilization: Ca-Stearate, Zn-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S4265 is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing intermediate bulk containers (IBC) for the packaging of dangerous goods, large blow molding parts, and jerry cans. This grade, produced with a 1-hexene co-monomer, offers very good creep strength, chemical resistance, environmental stress cracking resistance (ESCR), good processability, and stiffness.
HDPE
"A109455F" is a high-density polyethylene with Butene-1 as comonomer. It is a high molar mass for blown film with very high stiffness and good tenacity. Stabilization: Ca-Stearate, Zn-Stearate, Irgafos168.
HDPE
HDPE S104261A is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing automotive fuel tanks. This grade, produced with a 1-hexene co-monomer, offers excellent creep strength, processability, environmental stress cracking resistance (ESCR), and stiffness.
HDPE
T-HD 105218 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer.
HDPE
"A104760" is a high-density polyethylene with Butene-1 as comonomer. The product has high density and high stiffness, good flow ability and impact strength, and good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
Reviews
There are no reviews yet.