J-10CRP100 N (PE100)
Product data sheet for HDPE made via Hostalen Process.
Characteristic Properties:
- Grade: J-10CRP100 N (PE100)
- Density: 0.946 – 0.950 g/cm³
- Melt Flow Rate (MFR): 0.19 – 0.25 g/10 min (190°C/5 kg)
Main Applications:
- Top-quality PE100 pressure pipes
- Pipes for gas and water transportation at higher pressure or with thinner walls than PE80 (UV stabilization and/or pigments during processing)
Additives:
- Antioxidant / Process stabilizer
- Lubricant (processing aid) / Acid scavenger
Material Properties
| Test/Composition | Typical Value | Unit | ASTM Method |
|---|---|---|---|
| Density | 0.948 | g/m³ | ISO1183 |
| FRR 21.6/5 | 28 | – | – |
| Hydrostatic Strength (80°C) | 5000 (4.5N/mm²) | h | ISO1167 |
| MFR190°/21.6 | 6.2 | g/10 min | ISO1133 |
| MFR190°/5 | 0.22 | g/10 min | ISO1133 |
| Notched Impact @ 23°C | 24 | mJ/mm² | ISO179/1eA |
Additional Notes:
- Material Properties: These data are typical values and should not be construed as actual product specifications. Users should conduct their own tests to confirm these properties.
- Testing Conditions:
- Test specimens are taken from compression molded sheets at 23°C.
- FRR values are statistical and calculated by dividing MFR values.
- Notch Impact Test specimen from compressed molded sheet at 23°C; the data quoted are average values.
Be the first to review “J-10CRP100 N (PE100)”
Related products
HDPE
"A104750" is a high-density polyethylene with Butene-1 as comonomer. It has high impact strength and slightly lower stiffness than BL3, with high stress cracking resistance (ESCR) even in contact with surfactants. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A104760" is a high-density polyethylene with Butene-1 as comonomer. The product has high density and high stiffness, good flow ability and impact strength, and good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
T-HD 105030 SA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer with a medium content of slip agent additive.
HDPE
"A108255" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, is easily processable, has high stiffness, and provides good stress cracking resistance (ESCR) with an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A106255" is a high-density polyethylene with Butene-1 as comonomer. It is a special grade for particularly high requirements like low temperature impact strength and stacking, good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168, HOE Wax PED191.
HDPE
HDPE S104261A is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing automotive fuel tanks. This grade, produced with a 1-hexene co-monomer, offers excellent creep strength, processability, environmental stress cracking resistance (ESCR), and stiffness.
HDPE
"A GD107255" is a high-density polyethylene with Propylene as comonomer. It has high impact strength and low warping tendency. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S5110 is a high molecular weight, high-density polyethylene with broad molecular weight distribution and 1-hexene as a co-monomer, specially developed for producing thin films with excellent strength and rigidity. This product is suitable for manufacturing high-strength grocery sacks, shopping bags, and high-quality thin films for uni/multi-wall packaging. Films produced with this grade can be readily treated and printed for high-quality graphics.
Reviews
There are no reviews yet.