J-109450F (EX5)
Product data sheet for HDPE made via Hostalen Process.
Characteristic Properties:
- Grade: J-109450F (EX5)
- Density: 0.947 – 0.951 g/cm³
- Melt Flow Rate (MFR): 0.23 – 0.33 g/10 min (190°C/5 kg)
Main Applications:
- Blown films with pepper-like quality
- Suitable for counter bags, carrier bags, and wrapping films
- Excellent processing quality
Additives:
- Antioxidant / Process stabilizer
- Lubricant (processing aid) / Acid scavenger
Material Properties
| Test/Composition | Typical Value | Unit | Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ISO1183 |
| Fish Eye Note | ≤3 | note | Internal |
| FRR 21.6/5 | 29 | – | – |
| MFR 190°/21.6 | 8.0 | g/10min | ISO1133 |
| MFR190°/5 | 0.28 | g/10min | ISO1133 |
Additional Notes:
- Material Properties: These data are typical values and should not be construed as actual product specifications. Users should conduct their own tests to confirm these properties.
- Applications: This grade is designed for high molar mass film applications where good stiffness and tenacity are required.
- Testing Conditions:
- Test specimens are taken from compression molded sheets at 23°C.
- FRR values are statistical and calculated by dividing MFR values.
- Notch Impact Test specimen from compressed molded sheet at 23°C; the data quoted are average values.
Be the first to review “J-109450F (EX5)”
Related products
HDPE
"A104760" is a high-density polyethylene with Butene-1 as comonomer. The product has high density and high stiffness, good flow ability and impact strength, and good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S104261A is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing automotive fuel tanks. This grade, produced with a 1-hexene co-monomer, offers excellent creep strength, processability, environmental stress cracking resistance (ESCR), and stiffness.
HDPE
"A107250" is a high-density polyethylene with Propylene as comonomer. It is easy flowing, low warpage, less hard and stiff than I1. Stabilization: Ca-Stearate, Irganox1010.
HDPE
HDPE SPE80+ is a high molecular weight, high-density polyethylene (HDPE) with high melt viscosity for extrusion. This grade, produced with a 1-hexene co-monomer, is classified as PE 80+ and provides excellent stress crack resistance (ESCR) along with very good long-term hydrostatic strength and good processability.
HDPE
"A107260" is a high-density polyethylene with Propylene as comonomer. It is very easy flowing, high density, hardness and stiffness, largely warpage-free, for mass product articles in rapid shot frequency. Stabilization: Ca-Stearate, MgO, Irganox1010, UM V13.
HDPE
"A107745" is a high-density polyethylene with Butene-1 as comonomer. It is a special grade. Stabilization: Ca-Stearate, Irganox1010, Irgafos168, Tinevin326, Tinevin622.
HDPE
"A108255" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, is easily processable, has high stiffness, and provides good stress cracking resistance (ESCR) with an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A GD107255" is a high-density polyethylene with Propylene as comonomer. It has high impact strength and low warping tendency. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.