HDPE S5020
HDPE S5020 is a high-density polyethylene with a broad molecular weight distribution, specially developed for small blow-molded bottles. Produced with 1-hexene as a co-monomer, it offers high stiffness, easy flow, very good ESCR, chemical resistance, and sufficient impact strength. HDPE S5020 is recommended for multipurpose blow molding processes and has been manufactured under Basell license.
HDPE S5020 is a high-density polyethylene with a broad molecular weight distribution, specially developed for small blow-molded bottles. Produced with 1-hexene as a co-monomer, it offers high stiffness, easy flow, very good ESCR, chemical resistance, and sufficient impact strength. HDPE S5020 is recommended for multipurpose blow molding processes and has been manufactured under Basell license.
General Information:
- Status: Commercial: Active
- Application: Multipurpose blow molding process, Small blow-molded bottles, Packaging of consumer and dangerous goods
- Form(s): Pellet
Attributes:
- Good ESCR
- Good Chemical Resistance
- High Stiffness
Additives:
- Antioxidant: Yes
- Processing Aid: No
- Antiblock: No
- Slip Agent: No
| Property | Typical Value | Unit | Test Method |
|---|---|---|---|
| Physical | |||
| High Load Melt Flow Index (190°C/21.6 kg) | 22 | g/10 min | ISO 1133 |
| Melt Flow Index (190°C/2.16 kg) | 0.3 | g/10 min | ISO 1133 |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Bulk Density | > 0.50 | g/cm³ | ISO 60 |
| Mechanical | |||
| Tensile Modulus of Elasticity | 1000 | MPa | ISO 527-1,2 |
| Tensile Stress at Yield | 25 | MPa | ISO 527-1,2 |
| Tensile Strain at Yield | 9 | % | ISO 527-1,2 |
| Tensile Impact Strength (Notched, -30°C) | 110 | kJ/m² | ISO 8256 |
| Ball Indentation Hardness (H 132/30) | 45 | MPa | ISO 2039-1 |
| ESCR | 150 | hr | Basell method |
| FNCT (3.5 MPa, 2% Arkopal N100, 80°C) | 6 | hr | ISO 16770 |
| Thermal | |||
| Deflection Temperature Under Load (0.45 MPa) | 75 | °C | ISO 75 |
| Deflection Temperature Under Load (1.8 MPa) | 43 | °C | ISO 75 |
| Melting Temperature | 131 | °C | ISO 3146 |
| Vicat Softening Temperature (50N) | 78 | °C | ISO 306 |
Recommended Process Conditions:
- Extruder Barrel Temperature: 170-200 °C
- Melt Temperature: 190-220 °C
- Processing Method: Extrusion Blow Molding; Thermoforming
Be the first to review “HDPE S5020”
Related products
HDPE
HDPE SPE80+ is a high molecular weight, high-density polyethylene (HDPE) with high melt viscosity for extrusion. This grade, produced with a 1-hexene co-monomer, is classified as PE 80+ and provides excellent stress crack resistance (ESCR) along with very good long-term hydrostatic strength and good processability.
HDPE
T-HD 105030 SA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer with a medium content of slip agent additive.
HDPE
T-HD 106040 UA is a high-density polyethylene copolymer containing butene-1 (C4) as comonomer with medium content of light stabilizer additive.
HDPE
"A105010 T2N" is a natural-colored high-density polyethylene with Butene-1 as comonomer. The product is classified as PE100 and shows good stress crack resistance properties (ESCR) combined with good impact strength. Stabilization: Ca-Stearate, Zn-Stearate, Irganox1010, Irgafos168.
HDPE
"A108255" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, is easily processable, has high stiffness, and provides good stress cracking resistance (ESCR) with an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A107745" is a high-density polyethylene with Butene-1 as comonomer. It is a special grade. Stabilization: Ca-Stearate, Irganox1010, Irgafos168, Tinevin326, Tinevin622.
HDPE
"A107746" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, very good impact strength, and optimum stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A104750" is a high-density polyethylene with Butene-1 as comonomer. It has high impact strength and slightly lower stiffness than BL3, with high stress cracking resistance (ESCR) even in contact with surfactants. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
Reviews
There are no reviews yet.