“A107746” is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, very good impact strength, and optimum stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
Applications:
- Large containers above 5 liters capacity, e.g., petrol tanks.
- For the manufacture of semi-finished products.
Properties Table:
| No. | Property | Units | Test Method | Value |
|---|---|---|---|---|
| 1 | MFI (190°C/5Kg) | g/10min | ISO 1133 | 0.2 ± 0.04 |
| 2 | MFI (190°C/21.6Kg) | g/10min | ISO 1133 | 4.0 ± 0.4 |
| 3 | FRR21.6/5 | —– | —– | 20 |
| 4 | Density | g/cm³ | ISO 1183 | 0.943 ± 0.002 |
| 5 | Notched Impact Strength | mJ/mm² | ISO 179/1eA | 25 |
| 6 | Swell Ratio | % | Internal Method | 150 ± 20 |
Be the first to review “A107746”
Related products
HDPE
"A GD107255" is a high-density polyethylene with Propylene as comonomer. It has high impact strength and low warping tendency. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S5510 is a high-density polyethylene, specially developed for large parts blow molding. Produced with 1-hexene as a co-monomer, it offers high stiffness, good processability, excellent parison melt strength, and good ESCR. HDPE S5510 has been manufactured under Basell license.
HDPE
T-HD 104005 EA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use as pipe coating applications. T-HD 104005 EA has the following characteristics:
HDPE
"A107255" is a high-density polyethylene with Butene-1 as comonomer. It is a high molar mass material with very good impact strength and stiffness, good stress cracking resistance (ESCR), and provides an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168, HOE Wax PED191.
HDPE
"A108255" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, is easily processable, has high stiffness, and provides good stress cracking resistance (ESCR) with an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S4265 is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing intermediate bulk containers (IBC) for the packaging of dangerous goods, large blow molding parts, and jerry cans. This grade, produced with a 1-hexene co-monomer, offers very good creep strength, chemical resistance, environmental stress cracking resistance (ESCR), good processability, and stiffness.
HDPE
"A106255" is a high-density polyethylene with Butene-1 as comonomer. It is a special grade for particularly high requirements like low temperature impact strength and stacking, good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168, HOE Wax PED191.
HDPE
HDPE1080 is a high molecular weight, high-density polyethylene (HDPE) with high melt viscosity for extrusion. This grade, which is produced by 1-hexene co-monomer, is classified as HDPE1080 and provides excellent stress crack resistance properties (ESCR) combined with very good long-term hydrostatic strength and good processability.