Product Overview
Grand Resource PPR-FC20 is a low-heat-seal-temperature coating grade with good processability and high adhesive strength.
Grade & Processing
Grade: PPR-FC20. Polymer family: polypropylene random copolymer. Extrusion coating.
Typical Applications
- Extrusion coating of woven bags
- Cloth/paper interlayers for chemical and cement bags
Technical Data
| Property | Typical value / specification | Unit | Test method |
|---|---|---|---|
| MFR, 230 °C/2.16 kg | 20.0 | g/10 min | GB/T 3682.1-2018 |
| Tensile stress at yield | COA | MPa | GB/T 1040.2-2022 |
| Flexural modulus | > 600 | MPa | GB/T 9341-2008 |
| Charpy notched impact, 23 °C | COA | kJ/m² | GB/T 1043.1-2008 |
| Yellowness index | ≤ 3.0 | — | GB/T 39822-2021 |
| Ash | ≤ 0.06 | wt% | GB/T 9345.1-2008 |
| Heat-deflection temperature | COA | °C | GB/T 1634.2-2019 |
Be the first to review “Grand Resource PPR-FC20”
Related products
Polypropylene
INEOS PP N00M-00: high-impact polypropylene copolymer grade N00M-00 with applications and complete supplied technical data.
Polypropylene
Jinneng PP HP500N is a polypropylene injection-moulding grade for daily goods, electrical components and toys.
Polypropylene
Oriental Energy PPH Y40: controlled-rheology polypropylene homopolymer grade PPH Y40 with applications and complete supplied technical data.
Polypropylene
LyondellBasell Pro-fax 7823: polypropylene impact copolymer grade Pro-fax 7823 with applications and complete supplied technical data.
Polypropylene
Jinneng PP HP550J is a raffia polypropylene grade for woven bags, bulk bags and strapping tapes.
Polypropylene
Sinopec Maoming PPH-T03 (T30S): polypropylene homopolymer yarn grade grade PPH-T03 (T30S) with applications and complete supplied technical data.
Polypropylene
Borouge Borstar RA150E: PP-R random copolymer grade RA150E with applications and complete supplied technical data.
Polypropylene
Grand Resource PPR-MT15: polypropylene random copolymer grade PPR-MT15 with applications and complete supplied technical data.
Reviews
There are no reviews yet.