J-104760 (BL3)
Product data sheet for HDPE made via Hostalen Process.
Characteristic Properties:
- Grade: J-104760 (BL3)
- Density: 0.942 – 0.956 g/cm³
- Melt Flow Rate (MFR): 0.9 – 1.5 g/10 min (190°C/5 kg)
Main Applications:
- Containers with capacities ranging from a few ml up to 10 liters
- Production of sheets for thermoforming
Additives:
- Antioxidant / Process stabilizer
- Lubricant / Acid scavenger
Material Properties
| Resin Properties | Unit | Typical Value | Test Method |
|---|---|---|---|
| Melt Index (21.6) | g/10 min | 23 | ISO 1133 |
| Melt Index (5) | g/10 min | 1.2 | ISO 1133 |
| FRR (21.6/5) | – | 19 | – |
| Density | g/cm³ | 0.954 | ISO 1183 |
Molded Properties
| Property | Unit | Typical Value | Test Method |
|---|---|---|---|
| Notched Impact @ 23°C | mJ/mm² | 9 | ISO 179/1 eA |
Additional Notes:
- Material Properties: Data provided here are typical values and should not be construed as actual product specifications. Users should conduct tests to confirm these properties.
- Applications: This grade is designed for blow molding applications where good stress-cracking resistance and high impact strength are needed.
Be the first to review “J-104760 (BL3)”
Related products
HDPE
"A107745" is a high-density polyethylene with Butene-1 as comonomer. It is a special grade. Stabilization: Ca-Stearate, Irganox1010, Irgafos168, Tinevin326, Tinevin622.
HDPE
"A107260" is a high-density polyethylene with Propylene as comonomer. It is very easy flowing, high density, hardness and stiffness, largely warpage-free, for mass product articles in rapid shot frequency. Stabilization: Ca-Stearate, MgO, Irganox1010, UM V13.
HDPE
HDPE1080 is a high molecular weight, high-density polyethylene (HDPE) with high melt viscosity for extrusion. This grade, which is produced by 1-hexene co-monomer, is classified as HDPE1080 and provides excellent stress crack resistance properties (ESCR) combined with very good long-term hydrostatic strength and good processability.
HDPE
"A107746" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, very good impact strength, and optimum stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S5020 is a high-density polyethylene with a broad molecular weight distribution, specially developed for small blow-molded bottles. Produced with 1-hexene as a co-monomer, it offers high stiffness, easy flow, very good ESCR, chemical resistance, and sufficient impact strength. HDPE S5020 is recommended for multipurpose blow molding processes and has been manufactured under Basell license.
HDPE
"AGC107260" is a high-density polyethylene with Propylene as comonomer. The product has good impact strength, good stress cracking resistance (ESCR), low warping, and good flow ability, as well as high density, hardness, and stiffness. Stabilization: Ca-Stearate, Irganox1010.
HDPE
T-HD 103840 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use in rotational molding applications. T-HD 103840 UA has the following characteristics:
HDPE
T-HD 105218 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer.