Product Name: T-HD 104005 EA
Description: T-HD 104005 EA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use as pipe coating applications. T-HD 104005 EA has the following characteristics:
- Good impact strength and chemical resistance
- High ESCR
Applications:
- Pipe coating applications
Physical and Mechanical Properties:
| Property | Unit | Test Method | Typical Value |
|---|---|---|---|
| MELT FLOW INDEX (2.16KG) | g/10min | ASTM D-1238 | 0.5 |
| DENSITY | gr/cm³ | ASTM D-1505 | 0.940 |
| TENSILE STRESS AT YIELD | MPA | ASTM D-638 | 17 |
| TENSILE STRESS AT BREAK | MPA | ASTM D-638 | 26 |
| ELONGATION AT BREAK | % | ASTM D-638 | 600 |
| O.I.T. | MIN | ASTM D-3895 | 45 |
| HARDNESS | – | ASTM D-2240 | 55 |
| MELTING POINT | °C | ASTM D-1525 | 125 |
| VICAT SOFTENING POINT | °C | ASTM D-1525 | 115 |
All above-mentioned data are typical values and are not to be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).
Grade Suffix (Additives Indication):
- EA: GENERAL ANTIOXIDANT
Be the first to review “T-HD 104005 EA”
Related products
HDPE
"A109455F" is a high-density polyethylene with Butene-1 as comonomer. It is a high molar mass for blown film with very high stiffness and good tenacity. Stabilization: Ca-Stearate, Zn-Stearate, Irgafos168.
HDPE
"A109450F" is a high-density polyethylene with Butene-1 as comonomer. It is a high molar mass for blown film with, in comparison to EX4, lower stiffness and increased tenacity. The product has good toughness, low gel level, and good tear strength. Stabilization: Ca-Stearate, Zn-Stearate, Irgafos168.
HDPE
"A108255" is a high-density polyethylene with Butene-1 as comonomer. It has a high molar mass, is easily processable, has high stiffness, and provides good stress cracking resistance (ESCR) with an excellent molding surface finish. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
T-HD 104440 EA is a high-density polyethylene copolymer suitable as a base resin for crosslinked polyethylene pipes.
HDPE
"A 107750" is a high-density polyethylene with propylene as comonomer. It is a medium molar mass with a narrow molar mass distribution. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A105010 T2N" is a natural-colored high-density polyethylene with Butene-1 as comonomer. The product is classified as PE100 and shows good stress crack resistance properties (ESCR) combined with good impact strength. Stabilization: Ca-Stearate, Zn-Stearate, Irganox1010, Irgafos168.
HDPE
"A104750" is a high-density polyethylene with Butene-1 as comonomer. It has high impact strength and slightly lower stiffness than BL3, with high stress cracking resistance (ESCR) even in contact with surfactants. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
T-HD 103840 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use in rotational molding applications. T-HD 103840 UA has the following characteristics: