Product Name: T-PPH YD 225
Description: PPH YD 225 is a homopolymer grade with isotactic degree around 94% in powder form without stabilizers. This grade has low molecular weight with good fluidity.
Applications: Good for spun bond process and stretchability. Used for staple fiber, diaper, sanitary towel, master batch, and injection molding.
Physical and Mechanical Properties:
| Property | Unit | Test Method | Typical Value |
|---|---|---|---|
| MFI (@230°C & 2.16KG) | GR/10MIN | ISO1133 | 22 |
| Density | GR/CM3 | ASTM D1505 | 0.9 |
| Isotactic Degree | % | ISO 9113 | >=94 |
| Ash Content | PPM(WT) | ISO 3451-1 | <=350 |
| Chlorine Content | PPM(WT) | ENCO METHOD | <=100 |
| Volatile Content | %WT | ENCO METHOD | <=0.2 |
| Bulk Density | GR/CM3 | ASTM D1895 | 0.43 |
| Tensile Strength at Yield | MPA | ISO 527 | 33 |
| Elongation at Yield | % | ISO 527 | 9 |
| Flexural Modulus | MPA | ISO 178 | 1450 |
| Notched Izod Impact (@23°C) | KJ/M2 | ISO 180/1A | 3 |
| Rockwell Hardness | R SCALE | ASTM D785 | 100 |
| HDT (@0.46N/mm2) | °C | ISO 75/B | 85 |
| Vicat Softening Point (10N) | °C | ISO 306A | 154 |
| Melting Point (DSC) | °C | ISO 11357-1 | 163 |
Note: All above-mentioned data are typical values and should not be construed as real specifications. Users should confirm results by their own tests. For more information about guaranteed items, please refer to S.S.S. (Standard Sales Specifications).
Be the first to review “T-PPH YD 225”
Related products
Polypropylene
PPH HD 225 is a homopolymer grade with isotactic degree around 94% in powder form without stabilizers. This grade has low molecular weight with good fluidity.
Polypropylene
T-PPH XD 045 is a homopolymer grade with an isotactic degree around 94% in powder form, without stabilizers. This grade has medium molecular weight and exceptional mechanical properties.
Reviews
There are no reviews yet.