Product Overview
Grand Resource PPR-MT40 is a high-transparency grade with good forming performance.
Grade & Processing
Grade: PPR-MT40. Polymer family: polypropylene random copolymer. Injection moulding.
Typical Applications
- Food containers
- Stationery
- Storage boxes
Technical Data
| Property | Typical value / specification | Unit | Test method |
|---|---|---|---|
| MFR, 230 °C/2.16 kg | 40.0 | g/10 min | GB/T 3682.1-2018 |
| Tensile stress at yield, 50 mm/min | ≥ 23.0 | MPa | GB/T 1040.2-2022 |
| Flexural modulus, 2 mm/min | ≥ 900 | MPa | GB/T 9341-2008 |
| Charpy notched impact strength, 23 °C | ≥ 3.0 | kJ/m² | GB/T 1043.1-2008 |
| Yellowness index | ≤ 3.0 | — | GB/T 39822-2021 |
| Ash | ≤ 0.06 | wt% | GB/T 9345.1-2008 |
| Haze, 1 mm | ≤ 18.0 | % | GB/T 2410-2008 |
| Heat-deflection temperature | ≥ 60 | °C | GB/T 1634.2-2019 |
Be the first to review “Grand Resource PPR-MT40”
Related products
Polypropylene
Donghua Energy PPH Y26: polypropylene homopolymer grade PPH Y26 with applications and complete supplied technical data.
Polypropylene
Grand Resource PPR-FC20: polypropylene random copolymer grade PPR-FC20 with applications and complete supplied technical data.
Polypropylene
Grand Resource PPR-MT60M: polypropylene random copolymer grade PPR-MT60M with applications and complete supplied technical data.
Polypropylene
PPH Y16 is an antistatic, heat-resistant polypropylene injection grade for automotive applications.
Polypropylene
Grand Resource PPR-MT15: polypropylene random copolymer grade PPR-MT15 with applications and complete supplied technical data.
Polypropylene
Grand Resource PPR-MT25: polypropylene random copolymer grade PPR-MT25 with applications and complete supplied technical data.
Polypropylene
Grand Resource PPR-MT10-2: polypropylene random copolymer grade PPR-MT10-2 with applications and complete supplied technical data.
Polypropylene
Oriental Energy PPH Y40: controlled-rheology polypropylene homopolymer grade PPH Y40 with applications and complete supplied technical data.
Reviews
There are no reviews yet.