HDPE S5510 is a high-density polyethylene, specially developed for large parts blow molding. Produced with 1-hexene as a co-monomer, it offers high stiffness, good processability, excellent parison melt strength, and good ESCR. HDPE S5510 has been manufactured under Basell license.
General Information:
- Status: Commercial: Active
- Application: Large Parts Blow Molding, Standard and Lightweight Jerry Cans, Open Top Drums (up to 110 liters)
- Form(s): Pellet
Attributes:
- Good ESCR
- Good Stiffness
- Good Processability
Additives:
- Antioxidant: Yes
- Processing Aid: No
- Antiblock: No
- Slip Agent: No
| Property | Typical Value | Unit | Test Method |
|---|---|---|---|
| Physical | |||
| High Load Melt Flow Index (190°C/21.6 kg) | 10 | g/10 min | ISO 1133 |
| Melt Flow Index (190°C/5 kg) | 0.50 | g/10 min | ISO 1133 |
| Density | 0.955 | g/cm³ | ISO 1183 |
| Bulk Density | > 0.50 | g/cm³ | ISO 60 |
| Mechanical | |||
| Tensile Modulus of Elasticity | 1000 | MPa | ISO 527-1,2 |
| Flexural Modulus – 1% Secant | 1000 | MPa | ASTM D790 |
| Tensile Stress at Yield | 27 | MPa | ISO 527-1,2 |
| Tensile Strain at Yield | 8 | % | ISO 527-1,2 |
| Tensile Stress at Break | 43 | MPa | ISO 527-1,2 |
| Ball Indentation Hardness | 49 | MPa | ISO 2039-1 |
| ESCR F50 (100% Igepal, Method B) | 110 | hr | ASTM D1693 |
| Impact | |||
| Tensile Impact Strength (Notched, -30°C) | 135 | kJ/m² | ISO 8256 |
| Izod Impact Strength (Notched, 23°C) | 22 | kJ/m² | ISO 180 |
| Thermal | |||
| Vicat Softening Temperature (10N) | 127 | °C | ISO 306 |
| Deflection Temperature Under Load (1.8 MPa) | 45 | °C | ISO 75 |
Recommended Process Conditions:
- Extruder Barrel Temperature: 180-220 °C
- Melt Temperature: 200-235 °C
Be the first to review “HDPE S5510”
Related products
HDPE
"A GD107255" is a high-density polyethylene with Propylene as comonomer. It has high impact strength and low warping tendency. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A107740F2" is a high-density polyethylene with Butene-1 as comonomer. It is a medium molecular mass with a narrow molar mass distribution. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S104261A is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing automotive fuel tanks. This grade, produced with a 1-hexene co-monomer, offers excellent creep strength, processability, environmental stress cracking resistance (ESCR), and stiffness.
HDPE
"A107250" is a high-density polyethylene with Propylene as comonomer. It is easy flowing, low warpage, less hard and stiff than I1. Stabilization: Ca-Stearate, Irganox1010.
HDPE
T-HD 106040 UA is a high-density polyethylene copolymer containing butene-1 (C4) as comonomer with medium content of light stabilizer additive.
HDPE
T-HD 104005 EA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use as pipe coating applications. T-HD 104005 EA has the following characteristics:
HDPE
T-HD 104440 EA is a high-density polyethylene copolymer suitable as a base resin for crosslinked polyethylene pipes.
HDPE
"A105010 T2N" is a natural-colored high-density polyethylene with Butene-1 as comonomer. The product is classified as PE100 and shows good stress crack resistance properties (ESCR) combined with good impact strength. Stabilization: Ca-Stearate, Zn-Stearate, Irganox1010, Irgafos168.
Reviews
There are no reviews yet.