HDPE S5020
HDPE S5020 is a high-density polyethylene with a broad molecular weight distribution, specially developed for small blow-molded bottles. Produced with 1-hexene as a co-monomer, it offers high stiffness, easy flow, very good ESCR, chemical resistance, and sufficient impact strength. HDPE S5020 is recommended for multipurpose blow molding processes and has been manufactured under Basell license.
HDPE S5020 is a high-density polyethylene with a broad molecular weight distribution, specially developed for small blow-molded bottles. Produced with 1-hexene as a co-monomer, it offers high stiffness, easy flow, very good ESCR, chemical resistance, and sufficient impact strength. HDPE S5020 is recommended for multipurpose blow molding processes and has been manufactured under Basell license.
General Information:
- Status: Commercial: Active
- Application: Multipurpose blow molding process, Small blow-molded bottles, Packaging of consumer and dangerous goods
- Form(s): Pellet
Attributes:
- Good ESCR
- Good Chemical Resistance
- High Stiffness
Additives:
- Antioxidant: Yes
- Processing Aid: No
- Antiblock: No
- Slip Agent: No
| Property | Typical Value | Unit | Test Method |
|---|---|---|---|
| Physical | |||
| High Load Melt Flow Index (190°C/21.6 kg) | 22 | g/10 min | ISO 1133 |
| Melt Flow Index (190°C/2.16 kg) | 0.3 | g/10 min | ISO 1133 |
| Density | 0.950 | g/cm³ | ISO 1183 |
| Bulk Density | > 0.50 | g/cm³ | ISO 60 |
| Mechanical | |||
| Tensile Modulus of Elasticity | 1000 | MPa | ISO 527-1,2 |
| Tensile Stress at Yield | 25 | MPa | ISO 527-1,2 |
| Tensile Strain at Yield | 9 | % | ISO 527-1,2 |
| Tensile Impact Strength (Notched, -30°C) | 110 | kJ/m² | ISO 8256 |
| Ball Indentation Hardness (H 132/30) | 45 | MPa | ISO 2039-1 |
| ESCR | 150 | hr | Basell method |
| FNCT (3.5 MPa, 2% Arkopal N100, 80°C) | 6 | hr | ISO 16770 |
| Thermal | |||
| Deflection Temperature Under Load (0.45 MPa) | 75 | °C | ISO 75 |
| Deflection Temperature Under Load (1.8 MPa) | 43 | °C | ISO 75 |
| Melting Temperature | 131 | °C | ISO 3146 |
| Vicat Softening Temperature (50N) | 78 | °C | ISO 306 |
Recommended Process Conditions:
- Extruder Barrel Temperature: 170-200 °C
- Melt Temperature: 190-220 °C
- Processing Method: Extrusion Blow Molding; Thermoforming
Be the first to review “HDPE S5020”
Related products
HDPE
"A104760" is a high-density polyethylene with Butene-1 as comonomer. The product has high density and high stiffness, good flow ability and impact strength, and good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
"A107740F2" is a high-density polyethylene with Butene-1 as comonomer. It is a medium molecular mass with a narrow molar mass distribution. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
T-HD 105030 SA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer with a medium content of slip agent additive.
HDPE
HDPE S4265 is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing intermediate bulk containers (IBC) for the packaging of dangerous goods, large blow molding parts, and jerry cans. This grade, produced with a 1-hexene co-monomer, offers very good creep strength, chemical resistance, environmental stress cracking resistance (ESCR), good processability, and stiffness.
HDPE
"A104750" is a high-density polyethylene with Butene-1 as comonomer. It has high impact strength and slightly lower stiffness than BL3, with high stress cracking resistance (ESCR) even in contact with surfactants. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
T-HD 104005 EA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use as pipe coating applications. T-HD 104005 EA has the following characteristics:
HDPE
T-HD 103840 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer. It is suitable for use in rotational molding applications. T-HD 103840 UA has the following characteristics:
HDPE
"A GD107255" is a high-density polyethylene with Propylene as comonomer. It has high impact strength and low warping tendency. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
Reviews
There are no reviews yet.