HDPE S104261A
HDPE S104261A is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing automotive fuel tanks. This grade, produced with a 1-hexene co-monomer, offers excellent creep strength, processability, environmental stress cracking resistance (ESCR), and stiffness.
HDPE S104261A is a high molecular weight, high-density polyethylene with broad molecular weight distribution, specially developed for producing automotive fuel tanks. This grade, produced with a 1-hexene co-monomer, offers excellent creep strength, processability, environmental stress cracking resistance (ESCR), and stiffness.
General Information:
- Status: Commercial: Active
- Application: Automotive fuel tanks, Non-fuel reservoirs
- Form(s): Pellet
Attributes:
- Outstanding ESCR
- Very Good Creep Strength
- Good Chemical Resistance
- High Impact Resistance
- Excellent Processability
- Excellent Low Temp. Impact Resistance
Additives:
- Antioxidant: Yes
- Processing Aid: No
- Antiblock: No
- Slip Agent: No
| Property | Typical Value | Unit | Test Method |
|---|---|---|---|
| Physical | |||
| High Load Melt Flow Index (190°C/21.6 kg) | 5.6 | g/10 min | ISO 1133 |
| Density | 0.947 | g/cm³ | ISO 1183 |
| Bulk Density | > 0.50 | g/cm³ | ISO 60 |
| Mechanical | |||
| Tensile Strength at Yield | 25 | MPa | ISO 527-1, -2 |
| Tensile Strength at Break | 45 | MPa | ISO 527-1, -2 |
| Elongation at Yield | 10 | % | ISO 527-1, -2 |
| Elongation at Break | > 1200 | % | ISO 527-1, -2 |
| Tensile Modulus of Elasticity | 800 | MPa | ISO 527-1, -2 |
| Flexural Modulus – 1% Secant | > 800 | MPa | ASTM D790 |
| ESCR F10 (10% Igepal, Method B) | > 2000 | hr | ASTM D1693 |
| FNCT (3.5 MPa, 2% Arkopal N100, 80°C) | > 80 | hr | ISO 16770 |
| Impact | |||
| Tensile Impact Strength (Notched, -30°C) | 167 | kJ/m² | ISO 8256 |
| Izod Impact Strength (Notched, 23°C) | 26 | kJ/m² | ISO 180 |
| Thermal | |||
| Melting Temperature | 130 | °C | ISO 3146 |
| Oxidation Induction Time (200°C) | > 50 | min | ISO 11357 |
| Vicat Softening Temperature (10N) | 126 | °C | ISO 306 |
| Deflection Temperature Under Load (0.45 MPa) | 68 | °C | ISO 75 |
| Deflection Temperature Under Load (1.8 MPa) | 50 | °C | ISO 75 |
Recommended Process Conditions:
- Processing Method: Extrusion Blow Molding; Thermoforming
- Extruder Barrel Temperature: 200-230 °C
- Melt Temperature: 205-240 °C
Be the first to review “HDPE S104261A”
Related products
HDPE
T-HD 105218 UA is a high-density polyethylene copolymer containing butene-1 (C4) as a comonomer.
HDPE
"A107250" is a high-density polyethylene with Propylene as comonomer. It is easy flowing, low warpage, less hard and stiff than I1. Stabilization: Ca-Stearate, Irganox1010.
HDPE
"AGC107260" is a high-density polyethylene with Propylene as comonomer. The product has good impact strength, good stress cracking resistance (ESCR), low warping, and good flow ability, as well as high density, hardness, and stiffness. Stabilization: Ca-Stearate, Irganox1010.
HDPE
"A106255" is a high-density polyethylene with Butene-1 as comonomer. It is a special grade for particularly high requirements like low temperature impact strength and stacking, good stress cracking resistance (ESCR). Stabilization: Ca-Stearate, Irganox1010, Irgafos168, HOE Wax PED191.
HDPE
T-HD 104440 EA is a high-density polyethylene copolymer suitable as a base resin for crosslinked polyethylene pipes.
HDPE
T-HD 106040 UA is a high-density polyethylene copolymer containing butene-1 (C4) as comonomer with medium content of light stabilizer additive.
HDPE
"A 107750" is a high-density polyethylene with propylene as comonomer. It is a medium molar mass with a narrow molar mass distribution. Stabilization: Ca-Stearate, Irganox1010, Irgafos168.
HDPE
HDPE S5510 is a high-density polyethylene, specially developed for large parts blow molding. Produced with 1-hexene as a co-monomer, it offers high stiffness, good processability, excellent parison melt strength, and good ESCR. HDPE S5510 has been manufactured under Basell license.